Engineering high-performance and air-stable PBTZT-stat-BDTT-8:PC61BM/PC71BM organic solar cells
2018-06-27
Journal of Materials Chemistry A 6(14):5746-5751 Apr 2018

Jeon, Il; Sakai, Ryohei; Seo, Seungju; Morse, Graham E.; Ueno, Hiroshi; Nakagawa, Takafumi; Qian, Yang; Maruyama, Shigeo; Matsuo, Yutaka

Abstract:
High-performance air-stable PBTZT-stat-BDTT-8 organic solar cells were fabricated using mixed C60/C70fullerene acceptors. Normal-architecture devices using PBTZT-stat-BDTT-8 with PC71BM produced a power conversion efficiency (PCE) of 9.38%. An inverted-architecture, which possesses higher stability, was fabricated using a more economical PC61BM and PC71BM mixture with solution-processed PEDOT:PSS on top and produced a PCE of 8.15%. Exploiting the viscous nature of PBTZT-stat-BDTT-8, the slow evaporation effect was utilised to achieve an even higher efficiency of 8.73%. A stability test was conducted under operating conditions and our devices showed remarkably higher stability compared with PTB7-based devices.

Last updated: Jul. 2018   |  Copyright © Hefei National Laboratory for Physical Sciences at the Microscale  |  Top  |  Site Map