Ultrahigh Energy Density in SrTiO3 Film Capacitors
ACS Appl. Mater. Interfaces 9(24):20484-20490 Jun 2017

Hou, Chuangming; Huang, Weichuan; Zhao, Wenbo; Zhang, Dalong; Yin, Yuewei; Li, Xiaoguang

Solid-state dielectric film capacitors with high-energy-storage density will further promote advanced electronic devices and electrical power systems toward miniaturization, lightweight, and integration. In this study, the influence of interface and thickness on energy storage properties of SrTiO3 (STO) films grown on La0.67Sr0.33MnO3 (LSMO) electrode are systematically studied. The cross-sectional high resolution transmission electron microscopy reveals an ion interdiffusion layer and oxygen vacancies at the STO/LSMO interface. The capacitors show good frequency stability and increased dielectric constant with increasing STO thickness (410–710 nm). The breakdown strength (Eb) increases with decreasing STO thickness and reaches 6.8 MV/cm. Interestingly, the Eb under positive field is enhanced significantly and an ultrahigh energy density up to 307 J/cm3 with a high efficiency of 89% is realized. The enhanced Eb may be related to the modulation of local electric field and redistribution of oxygen vacancies at the STO/LSMO interface. Our results should be helpful for potential strategies to design devices with ultrahigh energy density.

Last updated: May. 2018   |  Copyright © Hefei National Laboratory for Physical Sciences at the Microscale  |  Top  |  Site Map