Breakthrough in Developing Electrocatalysts for CO2 Reduction through Elemental Doping
2018-08-18

The research group of Prof. ZENG Jie from School of Chemistry and Materials Science and Hefei National Laboratory for Physical Sciences at the Microscale has made a breakthrough in the preparation of formate and CO from electrochemical reduction of CO2 by using Ni doped SnS2 nanosheets with different doping contents as electrocatalysts. SnS2 nanosheets with appropriate Ni content were shown to possess enhanced activity and selectivity toward CO2 electrochemical reduction. This work was published onAngew. Chem. Int. Ed (Angew. Chem. Int. Ed.2018, 57, 10954-10958) entitled as“Nickel Doping in Atomically Thin Tin Disulfide Nanosheets Enables Highly Efficient CO2 Reduction”. Graduate students ZHANG An, HE Rong, and LI Huiping were the co-first authors of this work.

In CO2 electroreduction, the critical bottleneck lies in the activation of CO2 into a radical anion (CO2•-) which requires a high reduction potential of -1.9 V vs NHE. Generally, the CO2 activation concerns an electron transfer from catalysts to a COmolecule, which was closely associated with the electronic structure of catalysts. A powerful method to tailor the electronic structure of catalysts is elemental doping, because the introduction of heteroatoms leads to the hybridization of energy levels between dopants and pristine catalysts. Therefore, elemental doping provided a promising opportunity to facilitate CO2 activation and thereby improve the performance of COelectroreduction by modifying the electronic structure of catalysts.

 The mapping spectra of Ni doped SnSnanosheets and the electrochemical performances for COreduction.

Herein, we modified atomically thin SnS2 nanosheets with Ni doping for enhanced performance towards CO2 electroreduction. The Ni doped SnS2 nanosheets exhibited higher current density and Faradaic efficiency (FE) for carbonaceous product than those of the pristine SnS2 nanosheets. When the Ni content was 5 atm %, the Ni doped SnS2 nanosheets achieved a remarkable FE of 93% for carbonaceous product with a current density of 19.6 mA cm-2 at -0.9 V vs RHE. During the potentiostatic test, the Ni doped SnS2 nanosheets remained a steady FE for carbonaceous product without obvious decay of current density. Mechanistic study revealed that Ni doping generated a defect level at conduction band edge and decreased the work function of SnSnanosheets, which benefited the activation of CO2 and accordingly improved the catalytic performance in CO2 electroreduction.

This work was supported by CAS, MOST of China, and National Natural Science Foundation of China.



Last updated: Sep. 2018   |  Copyright © Hefei National Laboratory for Physical Sciences at the Microscale  |  Top  |  Site Map